| Customization: | Available |
|---|---|
| Type: | Stainless Steel Sheets |
| Standard: | ASTM, AISI |
|
Still deciding? Get samples of US$ 5/kg
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Product name |
S45503 S46500 S46910 stainless steel plate/sheet | |||
| Mode | S45503 S46500 S46910 | |||
| Rd &Material | ASTM A240 Standard | 201, 304 304L 304H 309S 309H 310S 310H 316 316H 316L 316Ti 317 317L 321 321H 347 347H 409 410 410S 430 904L | ||
| ASTM A480 Standard | 302, s30215, s30452, s30615, 308, 309, 309Cb, 310, 310Cb, S32615,S33228, S38100, 304H, 309H, 310H, 316H, 309HCb, 310HCb, 321H,347H, 348H, S31060, N08811, N08020, N08367, N08810, N08904,N08926, S31277, S20161, S30600, S30601, S31254, S31266,S32050, S32654, S32053, S31727, S33228, S34565, S35315,S31200, S31803, S32001, S32550, S31260, S32003, S32101,S32205, S32304, S32506, S32520, S32750, S32760, S32900, S32906, S32950, S32974 | |||
| JIS 4304-2005 Standard | SUS301L,SUS301J1,SUS302,SUS304, SUS304L, SUS316/316L, SUS309S, SUS310S, 3SUS21L, SUS347, SUS410L, SUS430, SUS630 | |||
| JIS G4305 Standard | SUS301, SUS301L, SUS301J1, SUS302B, SUS304, SUS304Cu,SUS304L, SUS304N1, SUS304N2, SUS304LN, SUS304J1, SUSJ2,SUS305, SUS309S, SUS310S, SUS312L, SUS315J1, SUS315J2,SUS316, SUS316L, SUS316N, SUS316LN, SUS316Ti, SUS316J1,SUS316J1L,SUS317, SUS317L, SUS317LN, SUS317J1, SUS317J2,SUS836L, SUS890L, SUS321, SUS347, SUSXM7, SUSXM15J1, SUS329J1, SUS329J3L, SUS329J4L, SUS405, SUS410L, SUS429, SUS430, SUS430LX, SUS430J1L, SUS434, SUS436L, SUS436J1L,SUS444, SUS445J1, SUS445J2, SUS447J1, SUSXM27, SUS403,SUS410, SUS410S, SUS420J1, SUS420J2, SUS440A | |||
| Finish | 2b, BA, No. 4, 8K, hairline, embossed, etched, vibration, PVD color coated, titanium, sand blasted, anti-fingerprint | |||
| Production technology | 1. Round steel preparation; 2. Heat; 3. Hot rolling perforation; 4. Cut the head; 5. Pickling; 6. Grinding; 7. Lubricate; 8. Cold rolling processing; 9. Degreasing; 10. Solution heat treatment; 11. Straightening; 12. Cut the tube; 13. Pickling; 14. Inspection of finished products. | |||
| Typical uses | Seawater equipment, chemicals, dyes, papermaking, oxalic acid, fertilizer and other production equipment; Photography, food industry, coastal facilities, ropes, CD rods, bolts, nuts. | |||
| Thickness | 1. Thin plate (0.2mm-4mm) 2. Middle plate (3mm-30mm) 3. Thick plate (4mm-60mm) 4. Extra thick plate (60-115mm) as customer's requirement | |||
|
Size |
as customer's requirement | |||
| Density | 7.98 g/cm³ | |||
| S45503 Chemical element content (%) | ||||||||||||
| Element | C | Si | Mn | P | S | Cr | Ni | Cu | Mo | N | Ti | Nb |
| Min | - | - | - | - | - | 11 | 7.5 | 1.5 | - | - | 1 | 0.1 |
| Max | 0.01 | 0.2 | 0.5 | 0.01 | 0.01 | 12.5 | 9.5 | 2.5 | 0.5 | 0.01 | 1.35 | 0.5 |
| S45503 Mechanical property | ||||||
| Condition | Heat treatment or condition | Tensile Strength | yield point | Elongation or elongation after breaking |
Elongation or elongation after breaking | Hardness |
| σb | σs | δ | ψ | HBW | ||
| Mpa | Mpa | % | % | |||
| steel | Solution treatment (A) :830± 15 °C quick cooling | HRC: ≤36 | ||||
| HB: ≤331 | ||||||
| Steel; t≤150 (longitudinal) | Quenching and/or aging (H900) :4h air cooling at 480°C | ≥1620 | ≥1520 | ≥8 | ≥30 | HRC: ≥47 |
| HB: ≥444 | ||||||
| Steel; t≤150 (horizontal) | Quenching and/or aging (H900) : 4h air-cooled at 480°C | ≥1620 | ≥1520 | ≥4 | ≥15 | HRC: ≥47 |
| HB: ≥444 | ||||||
| Steel; t≤150 (longitudinal) | Quenching and/or aging (H950) :510°C for 4h air cooling | ≥1515 | ≥1410 | ≥10 | ≥40 | HRC: ≥44 |
| HB: ≥415 | ||||||
| Steel; t≤150 (horizontal) | Quenching and/or aging (H950) :510°C for 4h air cooling | ≥1515 | ≥1410 | ≥5 | ≥20 | HRC: ≥44 |
| HB: ≥415 | ||||||
| Steel; t≤150 (longitudinal) | Quenching and/or aging (H1000) :540°C for 4h air-cooled | ≥1410 | ≥1275 | ≥10 | ≥40 | HRC: ≥40 |
| HB: ≥363 | ||||||
| Steel; t≤150 (horizontal) | Quenching and/or aging (H1000) :540°C for 4h air-cooled | ≥1410 | ≥1275 | ≥6 | ≥25 | HRC: ≥40 |
| HB: ≥363 | ||||||
| • Rockwell and Brinell hardness are both allowed. Size 12.7mm and below, Rockwell hardness HRC preferred. | ||||||
| S46500 Chemical element content (%) | ||||||||||
| Element | C | Si | Mn | P | S | Cr | Ni | Mo | N | Ti |
| Min | - | - | - | - | - | 11 | 10.75 | 0.75 | - | 1.5 |
| Max | 0.02 | 0.25 | 0.25 | 0.015 | 0.01 | 12.5 | 11.25 | 1.25 | 0.01 | 1.8 |
| S46500 Mechanical property | ||||||
| Condition | Heat treatment or condition | Tensile Strength | yield point | Elongation or elongation after breaking | percentage reduction of area | Hardness |
| σb | σs | δ | ψ | HBW | ||
| Mpa | Mpa | % | % | |||
| Steel | Solution treatment (A) :980 ± 15 °C oil or water quenching, 37°C for at least 8h, slow cooling | HRC: ≤36 | ||||
| HB: ≤331 | ||||||
| Steel | Solution treatment (A) :980 ± 15 °C oil or water quenching, 37°C for at least 8h, slow cooling + cold hardening (CW) | HRC: ≤40 | ||||
| HB: ≤380 | ||||||
| Steel; t≤300 (longitudinal) | Quenching and/or aging (H950) :510°C for 4h empty or oil cold | ≥1665 | ≥1515 | ≥10 | ≥45 | HRC: ≥47 |
| HB: ≥444 | ||||||
| Steel; t≤300 (horizontal) | Quenching and/or aging (H950) :510°C for 4h empty or oil cold | ≥1665 | ≥1515 | ≥8 | ≥35 | HRC: ≥47 |
| HB: ≥444 | ||||||
| Steel; t≤300 (longitudinal) | Quenching and/or aging (H1000) :540°C for 4h empty or oil cold | ≥1515 | ≥1380 | ≥10 | ≥50 | HRC: ≥45 |
| HB: ≥430 | ||||||
| Steel; t≤300 (horizontal) | Quenching and/or aging (H1000) :540°C for 4h empty or oil cold | ≥1515 | ≥1380 | ≥10 | ≥40 | HRC: ≥45 |
| HB: ≥430 | ||||||
| Steel; t≤300 (longitudinal) | Quenching and/or aging (H1025) :560°C for 4h empty or oil cold | ≥1450 | ≥1345 | ≥12 | ≥50 | HRC: ≥44 |
| HB: ≥415 | ||||||
| Steel; t≤300 (horizontal) | Quenching and/or aging (H1025) :560°C for 4h empty or oil cold | ≥1450 | ≥1345 | ≥11 | ≥45 | HRC: ≥44 |
| HB: ≥415 | ||||||
| Steel; t≤300 (longitudinal) | Quenching and/or aging (H1050) :565°C for 4h empty or oil cold | ≥1380 | ≥1280 | ≥13 | ≥50 | HRC: ≥43 |
| HB: ≥400 | ||||||
| Steel; t≤300 (horizontal) | Quenching and/or aging (H1050) :565°C for 4h empty or oil cold | ≥1380 | ≥1280 | ≥12 | ≥45 | HRC: ≥43 |
| HB: ≥400 | ||||||
| Steel; t≤25.4 (longitudinal) | Solution (A) + cold working (CW) + quenching and/or aging (H900) :482°C for 4h air or oil cold | ≥1755 | ≥1620 | ≥7 | ≥44 | HRC: ≥49 |
| HB: ≥455 | ||||||
| Steel; t≤25.4 (longitudinal) | Solution (A) + cold working (CW) + quenching and/or aging (H950) :510°C for 4h air or oil cold | ≥1720 | ≥1585 | ≥8 | ≥45 | HRC: ≥48 |
| HB: ≥450 | ||||||
| Steel; t≤25.4 (longitudinal) | Solution (A) + cold working (CW) + quenching and/or aging (H1000) :540°C for 4h air or oil cold | ≥1620 | ≥1480 | ≥9 | ≥50 | HRC: ≥46 |
| HB: ≥435 | ||||||
| Steel; t≤25.4 (longitudinal) | Solution (A) + cold working (CW) + quenching and/or aging (H1025) :560°C for 4h air or oil cold | ≥1550 | ≥1410 | ≥10 | ≥50 | HRC: ≥45 |
| HB: ≥425 | ||||||
| Steel; t≤25.4 (longitudinal) | Solution (A) + cold working (CW) + quenching and/or aging (H1050) :565°C for 4h air or oil cold | ≥1450 | ≥1310 | ≥10 | ≥50 | HRC: ≥44 |
| HB: ≥415 | ||||||
| • Rockwell and Brinell hardness are both allowed. Size 12.7mm and below, Rockwell hardness HRC preferred. | ||||||
| S46910 Chemical Element Content (%) | |||||||||||
| Element | C | Si | Mn | P | S | Cr | Ni | Cu | Mo | Ti | Al |
| Min | - | - | - | - | - | 11 | 8 | 1.5 | 3 | 0.5 | 0.15 |
| Max | 0.03 | 0.7 | 1 | 0.03 | 0.015 | 13 | 10 | 3.5 | 5 | 1.2 | 0.5 |
| S46910 Mechanical properties | |||||
| Condition | Heat treatment or condition | Tensile Strength | yield point | Elongation or elongation after breaking | Hardness |
| σb | σs | δ | HBW | ||
| Mpa | Mpa | % | |||
| Steel | Solution treatment (A) :1000~1120°C rapid cooling | ≥600 | ≥400 | ≥10 | HRC: ≤33 |
| HB: ≤315 | |||||
| Steel | Solution treatment (A) :1000~1120°C rapid cooling + cold hardening (CW-1/2 hard) | ≥900 | ≥750 | ≥8 | HRC: ≤40 |
| HB: ≤380 | |||||
| Steel | Solution treatment (A) :1000~1120°C rapid cooling + cold hardening (CW-hard) | ≥1300 | ≥1200 | ≥3 | HRC: ≤55 |
| HB: ≤580 | |||||
| Steel | Cold hardening (CW-1/2 hard) + aging 475°C for 1h air cooling | ≥1690 | ≥1500 | ≥6 | HRC: ≤48 |
| HB: ≤456 | |||||
| Steel | Cold hardening (CW-hard) + aging 475°C for 1h air cooling | ≥2205 | ≥2005 | ≥2 | HRC: ≤55 |
| HB: ≤561 | |||||
| • Rockwell and Brinell hardness are both allowed. Size 12.7mm and below, Rockwell hardness HRC preferred. | |||||
Premium Quality Materials:
We employ only the finest raw materials, ensuring that our products deliver unmatched strength, durability, and longevity.
Cutting-Edge Technology:
Our manufacturing techniques are at the forefront of innovation, featuring advanced smelting, continuous casting, and state-of-the-art rolling technologies.
Bespoke Service Solutions:
We provide customized design and manufacturing solutions tailored to fulfill the unique specifications and demands of our clients.
Frequently Asked Questions
Q1: Why should you choose our company?
A: With over 16 years of professional experience and our own manufacturing facility, we offer unparalleled service supported by a proficient and committed sales team.
Q2: What payment terms do you offer?
A: We require a 30% T/T deposit initially, with the remaining 70% payable before delivery.
Q3: What delivery terms do you offer?
A: We provide delivery terms including FOB, CFR, CIF, and EXW.
Q4: What is your standard delivery time?
A: Our typical delivery timeframe is 7 to 15 days following receipt of the deposit.
Q5: Are samples available?
A: Absolutely, we offer free samples when available in stock, though the buyer is responsible for the transportation costs.